CR012A Copper vs. SAE-AISI 1070 Steel

CR012A copper belongs to the copper alloys classification, while SAE-AISI 1070 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CR012A copper and the bottom bar is SAE-AISI 1070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
10 to 13
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
72
Tensile Strength: Ultimate (UTS), MPa 220
640 to 760
Tensile Strength: Yield (Proof), MPa 130
420 to 560

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1090
1460
Melting Onset (Solidus), °C 1040
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 390
50
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
10
Electrical Conductivity: Equal Weight (Specific), % IACS 100
12

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 360
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
59 to 86
Resilience: Unit (Modulus of Resilience), kJ/m3 76
470 to 850
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 6.8
23 to 27
Strength to Weight: Bending, points 9.0
21 to 24
Thermal Diffusivity, mm2/s 110
14
Thermal Shock Resistance, points 7.8
21 to 25

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0.65 to 0.75
Copper (Cu), % 99.85 to 99.94
0
Iron (Fe), % 0
98.3 to 98.8
Manganese (Mn), % 0
0.6 to 0.9
Oxygen (O), % 0 to 0.040
0
Phosphorus (P), % 0
0 to 0.040
Silver (Ag), % 0.060 to 0.080
0
Sulfur (S), % 0
0 to 0.050