CR016A Copper vs. Grade 33 Titanium
CR016A copper belongs to the copper alloys classification, while grade 33 titanium belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is CR016A copper and the bottom bar is grade 33 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 15 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 320 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1660 |
| Melting Onset (Solidus), °C | 1040 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 540 |
| Thermal Conductivity, W/m-K | 390 | |
| 21 |
| Thermal Expansion, µm/m-K | 17 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 98 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 6.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 55 |
| Density, g/cm3 | 9.0 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 33 |
| Embodied Energy, MJ/kg | 42 | |
| 530 |
| Embodied Water, L/kg | 390 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 86 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 83 | |
| 590 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 35 |
| Strength to Weight: Axial, points | 7.1 | |
| 24 |
| Strength to Weight: Bending, points | 9.3 | |
| 26 |
| Thermal Diffusivity, mm2/s | 110 | |
| 8.7 |
| Thermal Shock Resistance, points | 8.1 | |
| 30 |
Alloy Composition
| Bismuth (Bi), % | 0 to 0.00050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 0.1 to 0.2 |
| Copper (Cu), % | 99.843 to 99.919 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 | |
| 0.35 to 0.55 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Palladium (Pd), % | 0 | |
| 0.010 to 0.020 |
| Phosphorus (P), % | 0.0010 to 0.0070 | |
| 0 |
| Ruthenium (Ru), % | 0 | |
| 0.020 to 0.040 |
| Silver (Ag), % | 0.080 to 0.12 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.1 to 99.52 |
| Residuals, % | 0 | |
| 0 to 0.4 |