CR017A Copper vs. Grade 704C Zirconium

CR017A copper belongs to the copper alloys classification, while grade 704C zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is CR017A copper and the bottom bar is grade 704C zirconium.

EN CR017A (CuAg0.04(OF)) Silver-Bearing Oxygen-Free Copper Grade 704C Cast Zirconium

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		97

Elongation at Break, %		15
Elongation at Break, %		11

Poisson's Ratio		0.34
Poisson's Ratio		0.34

Shear Modulus, GPa		43
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		230
Tensile Strength: Ultimate (UTS), MPa		470

Tensile Strength: Yield (Proof), MPa		140
Tensile Strength: Yield (Proof), MPa		310

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		240

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		270

Thermal Conductivity, W/m-K		380
Thermal Conductivity, W/m-K		21

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		5.9

Otherwise Unclassified Properties

Density, g/cm³		9.0
Density, g/cm³		6.7

Embodied Water, L/kg		340
Embodied Water, L/kg		460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		31
Resilience: Ultimate (Unit Rupture Work), MJ/m³		48

Resilience: Unit (Modulus of Resilience), kJ/m³		83
Resilience: Unit (Modulus of Resilience), kJ/m³		490

Stiffness to Weight: Axial, points		7.2
Stiffness to Weight: Axial, points		8.1

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		7.1
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		9.3
Strength to Weight: Bending, points		20

Thermal Diffusivity, mm²/s		110
Thermal Diffusivity, mm²/s		12

Thermal Shock Resistance, points		8.1
Thermal Shock Resistance, points		58

Alloy Composition

Bismuth (Bi), %		0 to 0.00050
Bismuth (Bi), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.1

Copper (Cu), %		99.944 to 99.97
Copper (Cu), %		0

Hafnium (Hf), %		0
Hafnium (Hf), %		0 to 4.5

Hydrogen (H), %		0
Hydrogen (H), %		0 to 0.0050

Iron (Fe), %		0
Iron (Fe), %		0 to 0.3

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.030

Oxygen (O), %		0
Oxygen (O), %		0 to 0.3

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.010

Silver (Ag), %		0.030 to 0.050
Silver (Ag), %		0

Tin (Sn), %		0
Tin (Sn), %		1.0 to 2.0

Zirconium (Zr), %		0
Zirconium (Zr), %		92.9 to 99