EN-MC21110 Magnesium vs. C28000 Muntz Metal
EN-MC21110 magnesium belongs to the magnesium alloys classification, while C28000 Muntz Metal belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN-MC21110 magnesium and the bottom bar is C28000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 100 |
| Elongation at Break, % | 2.8 to 6.7 | |
| 10 to 45 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 18 | |
| 40 |
| Shear Strength, MPa | 120 to 160 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 270 | |
| 330 to 610 |
| Tensile Strength: Yield (Proof), MPa | 100 to 120 | |
| 150 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 120 |
| Melting Completion (Liquidus), °C | 600 | |
| 900 |
| Melting Onset (Solidus), °C | 500 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 390 |
| Thermal Conductivity, W/m-K | 80 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 61 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 23 |
| Density, g/cm3 | 1.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 2.7 |
| Embodied Energy, MJ/kg | 160 | |
| 46 |
| Embodied Water, L/kg | 990 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.9 to 14 | |
| 27 to 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 150 | |
| 110 to 670 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 69 | |
| 20 |
| Strength to Weight: Axial, points | 33 to 44 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 45 to 54 | |
| 13 to 20 |
| Thermal Diffusivity, mm2/s | 47 | |
| 40 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 11 to 20 |
Alloy Composition
| Aluminum (Al), % | 7.0 to 8.7 | |
| 0 |
| Copper (Cu), % | 0 to 0.030 | |
| 59 to 63 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 89.6 to 92.6 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.35 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0.35 to 1.0 | |
| 36.3 to 41 |
| Residuals, % | 0 | |
| 0 to 0.3 |