EN-MC21110 Magnesium vs. C87900 Brass

EN-MC21110 magnesium belongs to the magnesium alloys classification, while C87900 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21110 magnesium and the bottom bar is C87900 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 46
110
Elongation at Break, % 2.8 to 6.7
25
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 18
41
Tensile Strength: Ultimate (UTS), MPa 200 to 270
480
Tensile Strength: Yield (Proof), MPa 100 to 120
240

Thermal Properties

Latent Heat of Fusion, J/g 350
190
Maximum Temperature: Mechanical, °C 130
130
Melting Completion (Liquidus), °C 600
930
Melting Onset (Solidus), °C 500
900
Specific Heat Capacity, J/kg-K 990
390
Thermal Conductivity, W/m-K 80
120
Thermal Expansion, µm/m-K 26
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
15
Electrical Conductivity: Equal Weight (Specific), % IACS 61
17

Otherwise Unclassified Properties

Base Metal Price, % relative 12
24
Density, g/cm3 1.7
8.1
Embodied Carbon, kg CO2/kg material 23
2.7
Embodied Energy, MJ/kg 160
46
Embodied Water, L/kg 990
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.9 to 14
100
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 150
270
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 69
20
Strength to Weight: Axial, points 33 to 44
17
Strength to Weight: Bending, points 45 to 54
17
Thermal Diffusivity, mm2/s 47
37
Thermal Shock Resistance, points 12 to 16
16

Alloy Composition

Aluminum (Al), % 7.0 to 8.7
0 to 0.15
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.050
Copper (Cu), % 0 to 0.030
63 to 69.2
Iron (Fe), % 0 to 0.0050
0 to 0.4
Lead (Pb), % 0
0 to 0.25
Magnesium (Mg), % 89.6 to 92.6
0
Manganese (Mn), % 0.1 to 0.35
0 to 0.15
Nickel (Ni), % 0 to 0.0020
0 to 0.5
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0 to 0.2
0.8 to 1.2
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
0 to 0.25
Zinc (Zn), % 0.35 to 1.0
30 to 36
Residuals, % 0 to 0.010
0