EN-MC21210 Magnesium vs. 6016 Aluminum
EN-MC21210 magnesium belongs to the magnesium alloys classification, while 6016 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is 6016 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 48 | |
| 55 to 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 69 |
| Elongation at Break, % | 14 | |
| 11 to 27 |
| Fatigue Strength, MPa | 70 | |
| 68 to 89 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 110 | |
| 130 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 200 to 280 |
| Tensile Strength: Yield (Proof), MPa | 90 | |
| 110 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 160 |
| Melting Completion (Liquidus), °C | 600 | |
| 660 |
| Melting Onset (Solidus), °C | 570 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 190 to 210 |
| Thermal Expansion, µm/m-K | 27 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 48 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 160 to 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 1.6 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 8.2 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 980 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 | |
| 29 to 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 92 | |
| 82 to 340 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 72 | |
| 51 |
| Strength to Weight: Axial, points | 32 | |
| 21 to 29 |
| Strength to Weight: Bending, points | 44 | |
| 29 to 35 |
| Thermal Diffusivity, mm2/s | 76 | |
| 77 to 86 |
| Thermal Shock Resistance, points | 11 | |
| 9.1 to 12 |
Alloy Composition
| Aluminum (Al), % | 1.6 to 2.6 | |
| 96.4 to 98.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.010 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 96.3 to 98.3 | |
| 0.25 to 0.6 |
| Manganese (Mn), % | 0.1 to 0.7 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 1.0 to 1.5 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |