EN-MC21230 Magnesium vs. EN 1.0536 Steel
EN-MC21230 magnesium belongs to the magnesium alloys classification, while EN 1.0536 steel belongs to the iron alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN-MC21230 magnesium and the bottom bar is EN 1.0536 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 63 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 190 |
| Elongation at Break, % | 10 | |
| 18 |
| Fatigue Strength, MPa | 99 | |
| 340 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 18 | |
| 73 |
| Shear Strength, MPa | 130 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 220 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 400 |
| Melting Completion (Liquidus), °C | 600 | |
| 1460 |
| Melting Onset (Solidus), °C | 520 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 470 |
| Thermal Conductivity, W/m-K | 72 | |
| 51 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 63 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 2.1 |
| Density, g/cm3 | 1.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 1.7 |
| Embodied Energy, MJ/kg | 160 | |
| 24 |
| Embodied Water, L/kg | 990 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 | |
| 690 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 71 | |
| 24 |
| Strength to Weight: Axial, points | 36 | |
| 25 |
| Strength to Weight: Bending, points | 48 | |
| 23 |
| Thermal Diffusivity, mm2/s | 43 | |
| 14 |
| Thermal Shock Resistance, points | 13 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 8.5 | |
| 0.010 to 0.050 |
| Carbon (C), % | 0 | |
| 0.16 to 0.22 |
| Copper (Cu), % | 0 to 0.010 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 97.2 to 98.4 |
| Magnesium (Mg), % | 90.5 to 94.4 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.6 | |
| 1.3 to 1.7 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.070 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Vanadium (V), % | 0 | |
| 0.080 to 0.15 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.010 | |
| 0 |