EN-MC65210 Magnesium vs. S45503 Stainless Steel
EN-MC65210 magnesium belongs to the magnesium alloys classification, while S45503 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN-MC65210 magnesium and the bottom bar is S45503 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 80 | |
| 410 to 500 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 190 |
| Elongation at Break, % | 2.8 | |
| 4.6 to 6.8 |
| Fatigue Strength, MPa | 110 | |
| 710 to 800 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 75 |
| Shear Strength, MPa | 150 | |
| 940 to 1070 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 1610 to 1850 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 1430 to 1700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 760 |
| Melting Completion (Liquidus), °C | 610 | |
| 1440 |
| Melting Onset (Solidus), °C | 540 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 470 |
| Thermal Expansion, µm/m-K | 26 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 3.4 |
| Embodied Energy, MJ/kg | 220 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.9 | |
| 82 to 110 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 59 | |
| 24 |
| Strength to Weight: Axial, points | 38 | |
| 57 to 65 |
| Strength to Weight: Bending, points | 47 | |
| 39 to 43 |
| Thermal Shock Resistance, points | 17 | |
| 56 to 64 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Copper (Cu), % | 0 to 0.030 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 72.4 to 78.9 |
| Magnesium (Mg), % | 92.6 to 95.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 7.5 to 9.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.2 |
| Silver (Ag), % | 2.0 to 3.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.0 to 1.4 |
| Unspecified Rare Earths, % | 2.0 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.010 | |
| 0 |