EN-MC95310 Magnesium vs. ASTM B817 Type I
EN-MC95310 magnesium belongs to the magnesium alloys classification, while ASTM B817 type I belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN-MC95310 magnesium and the bottom bar is ASTM B817 type I.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 100 |
| Elongation at Break, % | 2.2 | |
| 4.0 to 13 |
| Fatigue Strength, MPa | 110 | |
| 360 to 520 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 17 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 770 to 960 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 700 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 340 |
| Melting Completion (Liquidus), °C | 650 | |
| 1600 |
| Melting Onset (Solidus), °C | 540 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 560 |
| Thermal Conductivity, W/m-K | 51 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 25 | |
| 9.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 36 |
| Density, g/cm3 | 1.9 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 38 |
| Embodied Energy, MJ/kg | 260 | |
| 610 |
| Embodied Water, L/kg | 900 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.6 | |
| 30 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 | |
| 2310 to 3540 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 61 | |
| 35 |
| Strength to Weight: Axial, points | 40 | |
| 48 to 60 |
| Strength to Weight: Bending, points | 49 | |
| 42 to 49 |
| Thermal Diffusivity, mm2/s | 28 | |
| 2.9 |
| Thermal Shock Resistance, points | 18 | |
| 54 to 68 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.4 |
| Lithium (Li), % | 0 to 0.2 | |
| 0 |
| Magnesium (Mg), % | 88.9 to 93.4 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.1 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 | |
| 87 to 91 |
| Unspecified Rare Earths, % | 1.5 to 4.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Yttrium (Y), % | 4.8 to 5.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |