EQ21A Magnesium vs. 224.0 Aluminum
EQ21A magnesium belongs to the magnesium alloys classification, while 224.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EQ21A magnesium and the bottom bar is 224.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 71 |
| Elongation at Break, % | 2.4 | |
| 4.0 to 10 |
| Fatigue Strength, MPa | 110 | |
| 86 to 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 250 | |
| 380 to 420 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 280 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 220 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 560 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 980 | |
| 870 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 27 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 11 |
| Density, g/cm3 | 1.9 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 8.3 |
| Embodied Energy, MJ/kg | 210 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.6 | |
| 16 to 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 | |
| 540 to 770 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 63 | |
| 45 |
| Strength to Weight: Axial, points | 37 | |
| 35 to 38 |
| Strength to Weight: Bending, points | 47 | |
| 38 to 41 |
| Thermal Diffusivity, mm2/s | 62 | |
| 47 |
| Thermal Shock Resistance, points | 15 | |
| 17 to 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 93 to 95.2 |
| Copper (Cu), % | 0.050 to 0.1 | |
| 4.5 to 5.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 93.9 to 96.8 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.060 |
| Silver (Ag), % | 1.3 to 1.7 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.35 |
| Unspecified Rare Earths, % | 1.5 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.15 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0.1 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.1 |