EV31A Magnesium vs. 355.0 Aluminum
EV31A magnesium belongs to the magnesium alloys classification, while 355.0 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is 355.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 70 | |
| 72 to 83 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 71 |
| Elongation at Break, % | 3.5 | |
| 1.5 to 2.6 |
| Fatigue Strength, MPa | 120 | |
| 55 to 70 |
| Poisson's Ratio | 0.27 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 27 |
| Shear Strength, MPa | 170 | |
| 150 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 200 to 260 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 150 to 190 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 180 |
| Melting Onset (Solidus), °C | 590 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 890 |
| Thermal Conductivity, W/m-K | 86 | |
| 150 to 170 |
| Thermal Expansion, µm/m-K | 27 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 38 to 43 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 90 | |
| 120 to 140 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 2.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 2.7 to 5.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 150 to 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 65 | |
| 51 |
| Strength to Weight: Axial, points | 40 | |
| 20 to 27 |
| Strength to Weight: Bending, points | 50 | |
| 28 to 33 |
| Thermal Diffusivity, mm2/s | 47 | |
| 60 to 69 |
| Thermal Shock Resistance, points | 16 | |
| 9.1 to 12 |