EV31A Magnesium vs. C47940 Brass
EV31A magnesium belongs to the magnesium alloys classification, while C47940 brass belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is C47940 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 100 |
| Elongation at Break, % | 3.5 | |
| 14 to 34 |
| Poisson's Ratio | 0.27 | |
| 0.31 |
| Shear Modulus, GPa | 17 | |
| 40 |
| Shear Strength, MPa | 170 | |
| 250 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 380 to 520 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 160 to 390 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 130 |
| Melting Onset (Solidus), °C | 590 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 380 |
| Thermal Conductivity, W/m-K | 86 | |
| 110 |
| Thermal Expansion, µm/m-K | 27 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 68 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 120 to 740 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 65 | |
| 19 |
| Strength to Weight: Axial, points | 40 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 50 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 47 | |
| 36 |
| Thermal Shock Resistance, points | 16 | |
| 13 to 17 |