Engineering Porcelain vs. Lithium Fluoride
Engineering porcelain belongs to the oxide-based engineering ceramics classification, while lithium fluoride belongs to the non-glass optical ceramics. There are 12 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is engineering porcelain and the bottom bar is lithium fluoride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 to 150 | |
| 120 |
| Poisson's Ratio | 0.17 | |
| 0.27 |
| Shear Modulus, GPa | 34 | |
| 52 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 600 to 1000 | |
| 1560 |
| Thermal Conductivity, W/m-K | 1.8 to 6.5 | |
| 12 |
| Thermal Expansion, µm/m-K | 2.0 to 6.6 | |
| 32 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.5 | |
| 9.0 |
| Electrical Dissipation At 1 MHz | 0.00043 to 0.013 | |
| 0.00020 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.3 to 3.0 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 16 to 29 | |
| 24 |
| Stiffness to Weight: Bending, points | 49 to 65 | |
| 62 |
| Thermal Diffusivity, mm2/s | 0.73 to 3.9 | |
| 2.9 |