Epoxy vs. POM-C
Epoxy belongs to the thermoset plastics classification, while POM-C belongs to the thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is epoxy and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 | |
| 1.4 to 1.6 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.4 | |
| 2.8 to 9.7 |
| Elongation at Break, % | 4.5 | |
| 3.0 to 65 |
| Limiting Oxygen Index (LOI), % | 20 | |
| 15 |
| Specific Heat Capacity, J/kg-K | 1500 | |
| 1130 to 1370 |
| Stiffness to Weight: Axial, points | 1.0 | |
| 1.1 to 3.3 |
| Stiffness to Weight: Bending, points | 34 | |
| 33 to 44 |
| Strength to Weight: Axial, points | 14 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 28 | |
| 24 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 67 | |
| 61 to 110 |