Ethyl Cellulose vs. PCTFE
Both Ethyl Cellulose and PCTFE are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is Ethyl Cellulose and the bottom bar is PCTFE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 2.1 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 55 to 93 | |
| 110 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 75 to 110 | |
| 130 |
| Impact Strength: Notched Izod, J/m | 66 to 220 | |
| 160 |
| Rockwell R Hardness | 56 to 130 | |
| 80 |
| Strength to Weight: Axial, points | 4.6 to 13 | |
| 4.6 |
| Strength to Weight: Bending, points | 14 to 27 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 18 to 51 | |
| 36 |
| Water Absorption After 24 Hours, % | 0.88 to 1.5 | |
| 0.0094 |