ECTFE vs. PTFE

Both ECTFE and PTFE are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is ECTFE and the bottom bar is PTFE.

Ethylene Chlorotrifluoroethylene (ECTFE)Polytetrafluoroethylene (PTFE)

Metric UnitsUS Customary Units

Mechanical Properties

Elongation at Break, %		230
Elongation at Break, %		75 to 300

Flexural Modulus, GPa		1.7
Flexural Modulus, GPa		0.4 to 1.3

Flexural Strength, MPa		47
Flexural Strength, MPa		13 to 50

Tensile Strength: Ultimate (UTS), MPa		49
Tensile Strength: Ultimate (UTS), MPa		13 to 25

Thermal Properties

Heat Deflection Temperature At 1.82 MPa (264 psi), °C		91
Heat Deflection Temperature At 1.82 MPa (264 psi), °C		66 to 70

Maximum Temperature: Mechanical, °C		150
Maximum Temperature: Mechanical, °C		260 to 270

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		330 to 340

Thermal Conductivity, W/m-K		0.15
Thermal Conductivity, W/m-K		0.24 to 0.65

Thermal Expansion, µm/m-K		100
Thermal Expansion, µm/m-K		110 to 120

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 MHz		2.6
Dielectric Constant (Relative Permittivity) At 1 MHz		2.1 to 2.4

Electrical Resistivity Order of Magnitude, 10^x Ω-m		14
Electrical Resistivity Order of Magnitude, 10^x Ω-m		2.0 to 18

Otherwise Unclassified Properties

Density, g/cm³		1.7
Density, g/cm³		2.1 to 2.3

Limiting Oxygen Index (LOI), %		60
Limiting Oxygen Index (LOI), %		90

Water Absorption After 24 Hours, %		0.094
Water Absorption After 24 Hours, %		0.0093 to 0.050

Common Calculations

Strength to Weight: Axial, points		8.1
Strength to Weight: Axial, points		1.7 to 3.2

Strength to Weight: Bending, points		18
Strength to Weight: Bending, points		5.7 to 8.7