Ferrite vs. Aluminosilicate Glass
Ferrite belongs to the oxide-based engineering ceramics classification, while aluminosilicate glass belongs to the glass and glass-ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is ferrite and the bottom bar is aluminosilicate glass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 4.7 to 4.8 | |
| 2.4 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 12 to 270 | |
| 6.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 120 to 140 | |
| 87 |
| Fracture Toughness, MPa-m1/2 | 1.4 to 1.5 | |
| 0.9 |
| Stiffness to Weight: Axial, points | 15 to 16 | |
| 20 |
| Stiffness to Weight: Bending, points | 35 to 36 | |
| 63 |