Forsterite vs. Magnesium Titanate
Both forsterite and magnesium titanate are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is forsterite and the bottom bar is magnesium titanate.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.1 to 3.1 | |
| 3.5 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.9 | |
| 9.1 |
| Electrical Dissipation At 1 MHz | 0.00030 | |
| 0.0013 |
| Flexural Strength, MPa | 40 to 160 | |
| 80 |
| Specific Heat Capacity, J/kg-K | 850 | |
| 950 |
| Thermal Conductivity, W/m-K | 1.7 to 3.5 | |
| 3.8 |
| Thermal Diffusivity, mm2/s | 0.94 to 1.3 | |
| 1.1 |
| Thermal Expansion, µm/m-K | 9.0 to 10 | |
| 8.0 |