Fused Silica vs. C-310 Titania-based Ceramic
Fused silica belongs to the glass and glass-ceramics classification, while C-310 titania-based ceramic belongs to the oxide-based engineering ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is fused silica and the bottom bar is C-310 titania-based ceramic.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.2 | |
| 3.7 |
| Dielectric Strength (Breakdown Potential), kV/mm | 30 | |
| 9.0 |
| Electrical Dissipation At 1 MHz | 0.00011 | |
| 0.0018 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 10 |
| Flexural Strength, MPa | 67 | |
| 75 |
| Specific Heat Capacity, J/kg-K | 720 | |
| 750 |
| Thermal Conductivity, W/m-K | 1.4 | |
| 3.5 |
| Thermal Diffusivity, mm2/s | 0.85 | |
| 1.3 |
| Thermal Expansion, µm/m-K | 0.5 | |
| 7.0 |