Glass-bonded Mica vs. SiAlON
Glass-bonded mica belongs to the glass and glass-ceramics classification, while SiAlON belongs to the non-oxide engineering ceramics. There are 19 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is glass-bonded mica and the bottom bar is SiAlON.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 270 | |
| 2620 |
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 290 |
| Flexural Strength, MPa | 79 | |
| 680 |
| Tensile Strength: Ultimate (UTS), MPa | 39 | |
| 190 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 450 | |
| 1200 |
| Maximum Thermal Shock, °C | 110 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 880 |
| Thermal Conductivity, W/m-K | 23 | |
| 19 |
| Thermal Expansion, µm/m-K | 6.7 | |
| 3.6 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.8 | |
| 9.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 20 | |
| 8.3 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 3.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 50 |
| Stiffness to Weight: Bending, points | 52 | |
| 67 |
| Strength to Weight: Axial, points | 4.1 | |
| 16 |
| Strength to Weight: Bending, points | 9.7 | |
| 22 |
| Thermal Diffusivity, mm2/s | 18 | |
| 6.4 |
| Thermal Shock Resistance, points | 5.9 | |
| 13 |