Grade 1 Titanium vs. SAE-AISI 4419 Steel

Grade 1 titanium belongs to the titanium alloys classification, while SAE-AISI 4419 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is grade 1 titanium and the bottom bar is SAE-AISI 4419 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
150
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 28
23
Fatigue Strength, MPa 170
190
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 39
73
Shear Strength, MPa 200
310
Tensile Strength: Ultimate (UTS), MPa 310
490
Tensile Strength: Yield (Proof), MPa 220
270

Thermal Properties

Latent Heat of Fusion, J/g 420
250
Maximum Temperature: Mechanical, °C 320
410
Melting Completion (Liquidus), °C 1660
1470
Melting Onset (Solidus), °C 1610
1420
Specific Heat Capacity, J/kg-K 540
470
Thermal Conductivity, W/m-K 20
50
Thermal Expansion, µm/m-K 8.8
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 37
2.4
Density, g/cm3 4.5
7.9
Embodied Carbon, kg CO2/kg material 31
1.5
Embodied Energy, MJ/kg 510
20
Embodied Water, L/kg 110
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79
97
Resilience: Unit (Modulus of Resilience), kJ/m3 230
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
24
Strength to Weight: Axial, points 19
17
Strength to Weight: Bending, points 23
18
Thermal Diffusivity, mm2/s 8.2
13
Thermal Shock Resistance, points 24
14

Alloy Composition

Carbon (C), % 0 to 0.080
0.18 to 0.23
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.2
98.1 to 98.8
Manganese (Mn), % 0
0.45 to 0.65
Molybdenum (Mo), % 0
0.45 to 0.6
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Titanium (Ti), % 99.095 to 100
0
Residuals, % 0 to 0.4
0