Grade 1 Babbitt Metal vs. C14510 Copper

Grade 1 Babbitt Metal belongs to the otherwise unclassified metals classification, while C14510 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 1 Babbitt Metal and the bottom bar is C14510 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 53
120
Elongation at Break, % 34
9.1 to 9.6
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 20
43
Tensile Strength: Yield (Proof), MPa 30
230 to 250

Thermal Properties

Latent Heat of Fusion, J/g 70
210
Melting Completion (Liquidus), °C 370
1080
Melting Onset (Solidus), °C 220
1050
Specific Heat Capacity, J/kg-K 230
390
Thermal Conductivity, W/m-K 45
360
Thermal Expansion, µm/m-K 21
17

Otherwise Unclassified Properties

Base Metal Price, % relative 75
33
Density, g/cm3 7.3
8.9
Embodied Carbon, kg CO2/kg material 12
2.6
Embodied Energy, MJ/kg 200
42
Embodied Water, L/kg 1160
310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 8.6
230 to 280
Stiffness to Weight: Axial, points 4.0
7.2
Stiffness to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 26
100

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 4.0 to 5.0
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0
Copper (Cu), % 4.0 to 5.0
99.15 to 99.69
Iron (Fe), % 0 to 0.080
0
Lead (Pb), % 0 to 0.35
0 to 0.050
Phosphorus (P), % 0
0.010 to 0.030
Tellurium (Te), % 0
0.3 to 0.7
Tin (Sn), % 89.3 to 92
0
Zinc (Zn), % 0 to 0.0050
0