Grade 15 Babbitt Metal vs. Type 1 Magnetic Alloy

Grade 15 Babbitt Metal belongs to the otherwise unclassified metals classification, while Type 1 magnetic alloy belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 15 Babbitt Metal and the bottom bar is Type 1 magnetic alloy.

Grade 15 (L53620) Lead-Base Babbitt Metal Type 1 (K94490) Iron-Nickel Soft Magnetic Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		23
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.4
Poisson's Ratio		0.3

Shear Modulus, GPa		8.2
Shear Modulus, GPa		72

Thermal Properties

Latent Heat of Fusion, J/g		46
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		280
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		250
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		140
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		17
Base Metal Price, % relative		31

Density, g/cm³		10
Density, g/cm³		8.3

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		5.6

Embodied Energy, MJ/kg		47
Embodied Energy, MJ/kg		77

Embodied Water, L/kg		840
Embodied Water, L/kg		130

Common Calculations

Stiffness to Weight: Axial, points		1.2
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		9.0
Stiffness to Weight: Bending, points		23

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		14.5 to 17.5
Antimony (Sb), %		0

Arsenic (As), %		0.8 to 1.4
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0
Chromium (Cr), %		0 to 0.3

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.5

Copper (Cu), %		0 to 0.6
Copper (Cu), %		0 to 0.3

Iron (Fe), %		0 to 0.1
Iron (Fe), %		50.7 to 56.5

Lead (Pb), %		79 to 83.9
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.8

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.3

Nickel (Ni), %		0
Nickel (Ni), %		43.5 to 46.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.010

Silicon (Si), %		0
Silicon (Si), %		0 to 0.5

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		0.8 to 1.2
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0