Grade 15 Babbitt Metal vs. K94200 Alloy
Grade 15 Babbitt Metal belongs to the otherwise unclassified metals classification, while K94200 alloy belongs to the iron alloys. There are 9 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is grade 15 Babbitt Metal and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 8.2 |
| Elastic (Young's, Tensile) Modulus, GPa | 23 | |
| 140 |
| Melting Onset (Solidus), °C | 250 | |
| 1440 |
| Poisson's Ratio | 0.4 | |
| 0.34 |
| Shear Modulus, GPa | 8.2 | |
| 54 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 500 |
| Stiffness to Weight: Axial, points | 1.2 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 21 |
| Thermal Expansion, µm/m-K | 26 | |
| 5.0 |