Grade 15 Babbitt Metal vs. R60704 Alloy
Both grade 15 Babbitt Metal and R60704 alloy are otherwise unclassified metals. There are 10 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is grade 15 Babbitt Metal and the bottom bar is R60704 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 6.7 |
| Elastic (Young's, Tensile) Modulus, GPa | 23 | |
| 97 |
| Embodied Water, L/kg | 840 | |
| 460 |
| Latent Heat of Fusion, J/g | 46 | |
| 240 |
| Poisson's Ratio | 0.4 | |
| 0.34 |
| Shear Modulus, GPa | 8.2 | |
| 36 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 270 |
| Stiffness to Weight: Axial, points | 1.2 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 23 |
| Thermal Expansion, µm/m-K | 26 | |
| 6.0 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 14.5 to 17.5 | |
| 0 |
| Arsenic (As), % | 0.8 to 1.4 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0.2 to 0.4 |
| Copper (Cu), % | 0 to 0.6 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.2 to 0.4 |
| Lead (Pb), % | 79 to 83.9 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Tin (Sn), % | 0.8 to 1.2 | |
| 1.0 to 2.0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 93 to 98.8 |