Grade 16 Titanium vs. 705.0 Aluminum
Grade 16 titanium belongs to the titanium alloys classification, while 705.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade 16 titanium and the bottom bar is 705.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 69 |
| Elongation at Break, % | 23 | |
| 8.4 to 10 |
| Fatigue Strength, MPa | 240 | |
| 63 to 98 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 38 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 400 | |
| 240 to 260 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 180 |
| Melting Completion (Liquidus), °C | 1660 | |
| 640 |
| Melting Onset (Solidus), °C | 1610 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 890 |
| Thermal Conductivity, W/m-K | 22 | |
| 140 |
| Thermal Expansion, µm/m-K | 9.2 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.2 | |
| 110 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 36 | |
| 8.4 |
| Embodied Energy, MJ/kg | 600 | |
| 150 |
| Embodied Water, L/kg | 230 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 | |
| 18 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 120 to 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 49 |
| Strength to Weight: Axial, points | 25 | |
| 24 to 26 |
| Strength to Weight: Bending, points | 27 | |
| 31 to 32 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 55 |
| Thermal Shock Resistance, points | 29 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 92.3 to 98.6 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.8 |
| Magnesium (Mg), % | 0 | |
| 1.4 to 1.8 |
| Manganese (Mn), % | 0 | |
| 0 to 0.6 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Titanium (Ti), % | 98.8 to 99.96 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 3.3 |
| Residuals, % | 0 | |
| 0 to 0.15 |