Grade 17 Titanium vs. Grade 3 Babbitt Metal
Grade 17 titanium belongs to the titanium alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is grade 17 titanium and the bottom bar is grade 3 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 56 |
| Poisson's Ratio | 0.32 | |
| 0.35 |
| Shear Modulus, GPa | 38 | |
| 21 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 46 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 79 |
| Melting Completion (Liquidus), °C | 1660 | |
| 420 |
| Melting Onset (Solidus), °C | 1610 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 230 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 36 | |
| 12 |
| Embodied Energy, MJ/kg | 600 | |
| 200 |
| Embodied Water, L/kg | 230 | |
| 1210 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 19 |
| Stiffness to Weight: Axial, points | 13 | |
| 4.2 |
| Stiffness to Weight: Bending, points | 35 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 7.5 to 8.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Copper (Cu), % | 0 | |
| 7.5 to 8.5 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.080 |
| Lead (Pb), % | 0 | |
| 0 to 0.35 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.18 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Tin (Sn), % | 0 | |
| 82.3 to 85 |
| Titanium (Ti), % | 99.015 to 99.96 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.4 | |
| 0 |