Grade 19 Titanium vs. ASTM B541 Gold
Grade 19 titanium belongs to the titanium alloys classification, while ASTM B541 gold belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 19 titanium and the bottom bar is ASTM B541 gold.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 5.6 to 17 | |
| 6.0 to 14 |
| Poisson's Ratio | 0.32 | |
| 0.4 |
| Shear Modulus, GPa | 47 | |
| 38 |
| Shear Strength, MPa | 550 to 750 | |
| 410 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1300 | |
| 670 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 480 to 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 90 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1110 |
| Melting Onset (Solidus), °C | 1600 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 170 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 17 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 to 150 | |
| 65 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3040 to 5530 | |
| 1090 to 3830 |
| Stiffness to Weight: Axial, points | 14 | |
| 3.4 |
| Stiffness to Weight: Bending, points | 33 | |
| 9.0 |
| Strength to Weight: Axial, points | 49 to 72 | |
| 11 to 19 |
| Strength to Weight: Bending, points | 41 to 53 | |
| 9.8 to 14 |
| Thermal Shock Resistance, points | 57 to 83 | |
| 36 to 63 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 13.5 to 15.5 |
| Gold (Au), % | 0 | |
| 70.5 to 72.5 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 8.0 to 9.0 |
| Silver (Ag), % | 0 | |
| 4.0 to 5.0 |
| Titanium (Ti), % | 71.1 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0.7 to 1.3 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |