Grade 19 Titanium vs. Commercially Pure Palladium
Grade 19 titanium belongs to the titanium alloys classification, while commercially pure palladium belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 19 titanium and the bottom bar is commercially pure palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 5.6 to 17 | |
| 1.1 to 11 |
| Poisson's Ratio | 0.32 | |
| 0.39 |
| Shear Modulus, GPa | 47 | |
| 43 |
| Shear Strength, MPa | 550 to 750 | |
| 120 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1300 | |
| 200 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 160 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1550 |
| Melting Onset (Solidus), °C | 1600 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 240 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 12 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 5.6 |
| Stiffness to Weight: Bending, points | 33 | |
| 14 |
| Strength to Weight: Axial, points | 49 to 72 | |
| 4.5 to 8.8 |
| Strength to Weight: Bending, points | 41 to 53 | |
| 6.2 to 9.7 |
| Thermal Shock Resistance, points | 57 to 83 | |
| 9.8 to 19 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 99.8 to 100 |
| Titanium (Ti), % | 71.1 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |