Grade 19 Titanium vs. Solder Alloy 116
Grade 19 titanium belongs to the titanium alloys classification, while solder alloy 116 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is grade 19 titanium and the bottom bar is solder alloy 116.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 26 |
| Elongation at Break, % | 5.6 to 17 | |
| 18 |
| Poisson's Ratio | 0.32 | |
| 0.42 |
| Shear Modulus, GPa | 47 | |
| 9.3 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1300 | |
| 34 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 34 |
| Melting Completion (Liquidus), °C | 1660 | |
| 260 |
| Melting Onset (Solidus), °C | 1600 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 160 |
| Thermal Conductivity, W/m-K | 6.2 | |
| 41 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 90 |
| Density, g/cm3 | 5.0 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 7.2 |
| Embodied Energy, MJ/kg | 760 | |
| 120 |
| Embodied Water, L/kg | 230 | |
| 690 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 33 | |
| 9.8 |
| Strength to Weight: Axial, points | 49 to 72 | |
| 0.94 |
| Strength to Weight: Bending, points | 41 to 53 | |
| 2.3 |
| Thermal Diffusivity, mm2/s | 2.4 | |
| 26 |
| Thermal Shock Resistance, points | 57 to 83 | |
| 3.4 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 68.4 to 70.5 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 29.5 to 30.5 |
| Titanium (Ti), % | 71.1 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |