Grade 19 Titanium vs. N08800 Stainless Steel
Grade 19 titanium belongs to the titanium alloys classification, while N08800 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade 19 titanium and the bottom bar is N08800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 5.6 to 17 | |
| 4.5 to 34 |
| Fatigue Strength, MPa | 550 to 620 | |
| 150 to 390 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 47 | |
| 77 |
| Shear Strength, MPa | 550 to 750 | |
| 340 to 580 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1300 | |
| 500 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 190 to 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 370 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1390 |
| Melting Onset (Solidus), °C | 1600 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 6.2 | |
| 12 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 30 |
| Density, g/cm3 | 5.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 5.3 |
| Embodied Energy, MJ/kg | 760 | |
| 76 |
| Embodied Water, L/kg | 230 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 to 150 | |
| 42 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3040 to 5530 | |
| 96 to 1740 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 33 | |
| 24 |
| Strength to Weight: Axial, points | 49 to 72 | |
| 18 to 35 |
| Strength to Weight: Bending, points | 41 to 53 | |
| 18 to 28 |
| Thermal Diffusivity, mm2/s | 2.4 | |
| 3.0 |
| Thermal Shock Resistance, points | 57 to 83 | |
| 13 to 25 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0.15 to 0.6 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.1 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 19 to 23 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 71.1 to 77 | |
| 0.15 to 0.6 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |