Grade 2 Titanium vs. AWS BVAu-2

Grade 2 titanium belongs to the titanium alloys classification, while AWS BVAu-2 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is grade 2 titanium and the bottom bar is AWS BVAu-2.

Grade 2 (3.7035, R50400) TitaniumAWS BVAu-2 (P00807) Vacuum Service Filler Metal
Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
100
Poisson's Ratio 0.32
0.4
Shear Modulus, GPa 38
36
Tensile Strength: Ultimate (UTS), MPa 420
150

Thermal Properties

Latent Heat of Fusion, J/g 420
92
Melting Completion (Liquidus), °C 1660
890
Melting Onset (Solidus), °C 1610
890
Specific Heat Capacity, J/kg-K 540
180
Thermal Expansion, µm/m-K 9.0
15

Otherwise Unclassified Properties

Density, g/cm3 4.5
17

Common Calculations

Stiffness to Weight: Axial, points 13
3.3
Stiffness to Weight: Bending, points 35
9.1
Strength to Weight: Axial, points 26
2.4
Strength to Weight: Bending, points 28
3.6
Thermal Shock Resistance, points 32
7.1

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.080
0 to 0.0050
Copper (Cu), % 0
19.5 to 20.5
Gold (Au), % 0
79.5 to 80.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.3
0
Lead (Pb), % 0
0 to 0.0020
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.0020
Titanium (Ti), % 98.9 to 100
0
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0