Grade 2 Babbitt Metal vs. C69300 Brass

Grade 2 Babbitt Metal belongs to the otherwise unclassified metals classification, while C69300 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade 2 Babbitt Metal and the bottom bar is C69300 brass.

Grade 2 (L13890) Tin-Base Babbitt Metal UNS C69300 Silicon Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		53
Elastic (Young's, Tensile) Modulus, GPa		110

Poisson's Ratio		0.35
Poisson's Ratio		0.32

Shear Modulus, GPa		19
Shear Modulus, GPa		41

Tensile Strength: Yield (Proof), MPa		42
Tensile Strength: Yield (Proof), MPa		300 to 390

Thermal Properties

Latent Heat of Fusion, J/g		72
Latent Heat of Fusion, J/g		240

Melting Completion (Liquidus), °C		350
Melting Completion (Liquidus), °C		880

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		860

Specific Heat Capacity, J/kg-K		230
Specific Heat Capacity, J/kg-K		400

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		19

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		26

Density, g/cm³		7.3
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		45

Embodied Water, L/kg		1240
Embodied Water, L/kg		310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		17
Resilience: Unit (Modulus of Resilience), kJ/m³		400 to 700

Stiffness to Weight: Axial, points		4.0
Stiffness to Weight: Axial, points		7.4

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		19

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		7.0 to 8.0
Antimony (Sb), %		0

Arsenic (As), %		0 to 0.1
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.080
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		3.0 to 4.0
Copper (Cu), %		73 to 77

Iron (Fe), %		0 to 0.080
Iron (Fe), %		0 to 0.1

Lead (Pb), %		0 to 0.35
Lead (Pb), %		0 to 0.090

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.1

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.1

Phosphorus (P), %		0
Phosphorus (P), %		0.040 to 0.15

Silicon (Si), %		0
Silicon (Si), %		2.7 to 3.4

Tin (Sn), %		87.3 to 90
Tin (Sn), %		0 to 0.2

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		18.4 to 24.3

Residuals, %		0
Residuals, %		0 to 0.5