Grade 2 Babbitt Metal vs. R60802 Alloy
Both grade 2 Babbitt Metal and R60802 alloy are otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is grade 2 Babbitt Metal and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 98 |
| Poisson's Ratio | 0.35 | |
| 0.34 |
| Shear Modulus, GPa | 19 | |
| 36 |
| Tensile Strength: Yield (Proof), MPa | 42 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 72 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 270 |
| Thermal Expansion, µm/m-K | 21 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 6.5 |
| Embodied Water, L/kg | 1240 | |
| 290 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 17 | |
| 380 |
| Stiffness to Weight: Axial, points | 4.0 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 17 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 7.0 to 8.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.15 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Iron (Fe), % | 0 to 0.080 | |
| 0.070 to 0.2 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.030 to 0.080 |
| Tin (Sn), % | 87.3 to 90 | |
| 1.2 to 1.7 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 97.8 to 98.7 |
| Residuals, % | 0 | |
| 0 to 0.11 |