Grade 20 Titanium vs. SAE-AISI 1023 Steel
Grade 20 titanium belongs to the titanium alloys classification, while SAE-AISI 1023 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade 20 titanium and the bottom bar is SAE-AISI 1023 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 5.7 to 17 | |
| 17 to 29 |
| Fatigue Strength, MPa | 550 to 630 | |
| 180 to 270 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Reduction in Area, % | 23 | |
| 46 to 56 |
| Shear Modulus, GPa | 47 | |
| 73 |
| Shear Strength, MPa | 560 to 740 | |
| 280 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 1270 | |
| 430 to 480 |
| Tensile Strength: Yield (Proof), MPa | 850 to 1190 | |
| 240 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 370 | |
| 400 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1460 |
| Melting Onset (Solidus), °C | 1600 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 52 | |
| 1.4 |
| Embodied Energy, MJ/kg | 860 | |
| 18 |
| Embodied Water, L/kg | 350 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 150 | |
| 77 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2940 to 5760 | |
| 150 to 450 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 33 | |
| 24 |
| Strength to Weight: Axial, points | 50 to 70 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 41 to 52 | |
| 16 to 17 |
| Thermal Shock Resistance, points | 55 to 77 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0.2 to 0.25 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 99.06 to 99.5 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 71 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |