Grade 20 Titanium vs. SAE-AISI 1330 Steel
Grade 20 titanium belongs to the titanium alloys classification, while SAE-AISI 1330 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade 20 titanium and the bottom bar is SAE-AISI 1330 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 5.7 to 17 | |
| 11 to 23 |
| Fatigue Strength, MPa | 550 to 630 | |
| 210 to 380 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 47 | |
| 73 |
| Shear Strength, MPa | 560 to 740 | |
| 330 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 1270 | |
| 520 to 710 |
| Tensile Strength: Yield (Proof), MPa | 850 to 1190 | |
| 290 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 370 | |
| 400 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1460 |
| Melting Onset (Solidus), °C | 1600 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 52 | |
| 1.4 |
| Embodied Energy, MJ/kg | 860 | |
| 19 |
| Embodied Water, L/kg | 350 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 150 | |
| 76 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2940 to 5760 | |
| 230 to 990 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 33 | |
| 24 |
| Strength to Weight: Axial, points | 50 to 70 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 41 to 52 | |
| 18 to 23 |
| Thermal Shock Resistance, points | 55 to 77 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0.28 to 0.33 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 97.3 to 98 |
| Manganese (Mn), % | 0 | |
| 1.6 to 1.9 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Titanium (Ti), % | 71 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |