Grade 200 Maraging Steel vs. 86.5-silver 13.5-cadmium-oxide
Grade 200 maraging steel belongs to the iron alloys classification, while 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is grade 200 maraging steel and the bottom bar is 86.5-silver 13.5-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.2 | |
| 10 |
| Elongation at Break, % | 9.1 to 18 | |
| 3.4 to 16 |
| Shear Strength, MPa | 600 to 890 | |
| 170 to 210 |
| Strength to Weight: Axial, points | 33 to 51 | |
| 7.6 to 11 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 9.3 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1500 | |
| 280 to 410 |