Grade 200 Maraging Steel vs. 90-silver 10-tin-oxide
Grade 200 maraging steel belongs to the iron alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is grade 200 maraging steel and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 9.1 to 18 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 20 to 68 |
| Shear Strength, MPa | 600 to 890 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1500 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 690 to 1490 | |
| 120 to 280 |