Grade 21 Titanium vs. C17500 Copper
Grade 21 titanium belongs to the titanium alloys classification, while C17500 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is grade 21 titanium and the bottom bar is C17500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
120 |
Elongation at Break, % | 9.0 to 17 | |
6.0 to 30 |
Fatigue Strength, MPa | 550 to 660 | |
170 to 310 |
Poisson's Ratio | 0.32 | |
0.34 |
Shear Modulus, GPa | 51 | |
45 |
Shear Strength, MPa | 550 to 790 | |
200 to 520 |
Tensile Strength: Ultimate (UTS), MPa | 890 to 1340 | |
310 to 860 |
Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
170 to 760 |
Thermal Properties
Latent Heat of Fusion, J/g | 410 | |
220 |
Maximum Temperature: Mechanical, °C | 310 | |
220 |
Melting Completion (Liquidus), °C | 1740 | |
1060 |
Melting Onset (Solidus), °C | 1690 | |
1020 |
Specific Heat Capacity, J/kg-K | 500 | |
390 |
Thermal Conductivity, W/m-K | 7.5 | |
200 |
Thermal Expansion, µm/m-K | 7.1 | |
18 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 60 | |
60 |
Density, g/cm3 | 5.4 | |
8.9 |
Embodied Carbon, kg CO2/kg material | 32 | |
4.7 |
Embodied Energy, MJ/kg | 490 | |
73 |
Embodied Water, L/kg | 180 | |
320 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 180 | |
30 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 2760 to 5010 | |
120 to 2390 |
Stiffness to Weight: Axial, points | 14 | |
7.5 |
Stiffness to Weight: Bending, points | 32 | |
18 |
Strength to Weight: Axial, points | 46 to 69 | |
9.7 to 27 |
Strength to Weight: Bending, points | 38 to 50 | |
11 to 23 |
Thermal Diffusivity, mm2/s | 2.8 | |
59 |
Thermal Shock Resistance, points | 66 to 100 | |
11 to 29 |
Alloy Composition
Aluminum (Al), % | 2.5 to 3.5 | |
0 to 0.2 |
Beryllium (Be), % | 0 | |
0.4 to 0.7 |
Carbon (C), % | 0 to 0.050 | |
0 |
Cobalt (Co), % | 0 | |
2.4 to 2.7 |
Copper (Cu), % | 0 | |
95.6 to 97.2 |
Hydrogen (H), % | 0 to 0.015 | |
0 |
Iron (Fe), % | 0 to 0.4 | |
0 to 0.1 |
Molybdenum (Mo), % | 14 to 16 | |
0 |
Niobium (Nb), % | 2.2 to 3.2 | |
0 |
Nitrogen (N), % | 0 to 0.030 | |
0 |
Oxygen (O), % | 0 to 0.17 | |
0 |
Silicon (Si), % | 0.15 to 0.25 | |
0 to 0.2 |
Titanium (Ti), % | 76 to 81.2 | |
0 |
Residuals, % | 0 | |
0 to 0.5 |