Grade 250 Maraging Steel vs. Type 1 Magnetic Alloy
Both grade 250 maraging steel and Type 1 magnetic alloy are iron alloys. They have 72% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade 250 maraging steel and the bottom bar is Type 1 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 7.3 to 17 | |
| 4.0 to 38 |
| Poisson's Ratio | 0.3 | |
| 0.3 |
| Shear Modulus, GPa | 75 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1800 | |
| 500 to 830 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1740 | |
| 220 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1420 |
| Melting Onset (Solidus), °C | 1430 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 31 |
| Density, g/cm3 | 8.2 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 5.6 |
| Embodied Energy, MJ/kg | 65 | |
| 77 |
| Embodied Water, L/kg | 140 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 33 to 150 |
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 33 to 61 | |
| 17 to 28 |
| Strength to Weight: Bending, points | 26 to 40 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 29 to 54 | |
| 16 to 26 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Cobalt (Co), % | 7.0 to 8.5 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 66.3 to 71.1 | |
| 50.7 to 56.5 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 to 0.3 |
| Nickel (Ni), % | 17 to 19 | |
| 43.5 to 46.5 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.3 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |