Grade 28 Titanium vs. EN AC-45300 Aluminum
Grade 28 titanium belongs to the titanium alloys classification, while EN AC-45300 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is grade 28 titanium and the bottom bar is EN AC-45300 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 11 to 17 | |
| 1.0 to 2.8 |
| Fatigue Strength, MPa | 330 to 480 | |
| 59 to 72 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 980 | |
| 220 to 290 |
| Tensile Strength: Yield (Proof), MPa | 540 to 810 | |
| 150 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 470 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 170 |
| Melting Completion (Liquidus), °C | 1640 | |
| 630 |
| Melting Onset (Solidus), °C | 1590 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 890 |
| Thermal Conductivity, W/m-K | 8.3 | |
| 150 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 9.5 |
| Density, g/cm3 | 4.5 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 37 | |
| 8.0 |
| Embodied Energy, MJ/kg | 600 | |
| 150 |
| Embodied Water, L/kg | 370 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 110 | |
| 2.7 to 5.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 to 3100 | |
| 160 to 390 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 50 |
| Strength to Weight: Axial, points | 43 to 61 | |
| 23 to 29 |
| Strength to Weight: Bending, points | 39 to 49 | |
| 30 to 35 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 60 |
| Thermal Shock Resistance, points | 47 to 66 | |
| 10 to 13 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.5 | |
| 90.2 to 94.2 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Copper (Cu), % | 0 | |
| 1.0 to 1.5 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.65 |
| Lead (Pb), % | 0 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 | |
| 0.35 to 0.65 |
| Manganese (Mn), % | 0 | |
| 0 to 0.55 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Silicon (Si), % | 0 | |
| 4.5 to 5.5 |
| Tin (Sn), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 92.4 to 95.4 | |
| 0 to 0.25 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |