Grade 29 Titanium vs. EN AC-21200 Aluminum
Grade 29 titanium belongs to the titanium alloys classification, while EN AC-21200 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is grade 29 titanium and the bottom bar is EN AC-21200 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 6.8 to 11 | |
| 3.9 to 6.2 |
| Fatigue Strength, MPa | 460 to 510 | |
| 110 to 130 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 940 | |
| 410 to 440 |
| Tensile Strength: Yield (Proof), MPa | 850 to 870 | |
| 270 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 340 | |
| 170 |
| Melting Completion (Liquidus), °C | 1610 | |
| 660 |
| Melting Onset (Solidus), °C | 1560 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 880 |
| Thermal Conductivity, W/m-K | 7.3 | |
| 130 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.0 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 10 |
| Density, g/cm3 | 4.5 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 39 | |
| 8.0 |
| Embodied Energy, MJ/kg | 640 | |
| 150 |
| Embodied Water, L/kg | 410 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 100 | |
| 16 to 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3420 to 3540 | |
| 500 to 930 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 46 |
| Strength to Weight: Axial, points | 58 to 59 | |
| 38 to 40 |
| Strength to Weight: Bending, points | 47 to 48 | |
| 41 to 43 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 49 |
| Thermal Shock Resistance, points | 68 to 69 | |
| 18 to 19 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 93.3 to 95.7 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Copper (Cu), % | 0 | |
| 4.0 to 5.0 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Magnesium (Mg), % | 0 | |
| 0.15 to 0.5 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.050 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 88 to 90.9 | |
| 0 to 0.1 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.1 |