Grade 29 Titanium vs. SAE-AISI 1151 Steel
Grade 29 titanium belongs to the titanium alloys classification, while SAE-AISI 1151 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is grade 29 titanium and the bottom bar is SAE-AISI 1151 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 6.8 to 11 | |
| 11 to 17 |
| Fatigue Strength, MPa | 460 to 510 | |
| 260 to 410 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Reduction in Area, % | 17 | |
| 34 to 40 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Shear Strength, MPa | 550 to 560 | |
| 430 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 940 | |
| 710 to 800 |
| Tensile Strength: Yield (Proof), MPa | 850 to 870 | |
| 390 to 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 340 | |
| 400 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1460 |
| Melting Onset (Solidus), °C | 1560 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 470 |
| Thermal Conductivity, W/m-K | 7.3 | |
| 51 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.0 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 1.8 |
| Density, g/cm3 | 4.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 39 | |
| 1.4 |
| Embodied Energy, MJ/kg | 640 | |
| 18 |
| Embodied Water, L/kg | 410 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 100 | |
| 86 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3420 to 3540 | |
| 400 to 1170 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 24 |
| Strength to Weight: Axial, points | 58 to 59 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 47 to 48 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 14 |
| Thermal Shock Resistance, points | 68 to 69 | |
| 22 to 25 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0.48 to 0.55 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 98.3 to 98.7 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0.080 to 0.13 |
| Titanium (Ti), % | 88 to 90.9 | |
| 0 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |