Grade 29 Titanium vs. N06250 Nickel
Grade 29 titanium belongs to the titanium alloys classification, while N06250 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade 29 titanium and the bottom bar is N06250 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 210 |
| Elongation at Break, % | 6.8 to 11 | |
| 46 |
| Fatigue Strength, MPa | 460 to 510 | |
| 230 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 82 |
| Shear Strength, MPa | 550 to 560 | |
| 500 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 940 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 850 to 870 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 340 | |
| 980 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1490 |
| Melting Onset (Solidus), °C | 1560 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 440 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 55 |
| Density, g/cm3 | 4.5 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 39 | |
| 10 |
| Embodied Energy, MJ/kg | 640 | |
| 140 |
| Embodied Water, L/kg | 410 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 100 | |
| 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3420 to 3540 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 23 |
| Strength to Weight: Axial, points | 58 to 59 | |
| 23 |
| Strength to Weight: Bending, points | 47 to 48 | |
| 21 |
| Thermal Shock Resistance, points | 68 to 69 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 20 to 23 |
| Copper (Cu), % | 0 | |
| 0.25 to 1.3 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 7.4 to 19.4 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 10.1 to 12 |
| Nickel (Ni), % | 0 | |
| 50 to 54 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.090 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 88 to 90.9 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.25 to 1.3 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |