Grade 3 Babbitt Metal vs. Grade CZ100 Nickel

Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while grade CZ100 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is grade CZ100 nickel.

Grade 3 (L13840) Tin-Base Babbitt Metal Grade CZ100 (J02100) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		56
Elastic (Young's, Tensile) Modulus, GPa		180

Poisson's Ratio		0.35
Poisson's Ratio		0.31

Shear Modulus, GPa		21
Shear Modulus, GPa		69

Tensile Strength: Yield (Proof), MPa		46
Tensile Strength: Yield (Proof), MPa		140

Thermal Properties

Latent Heat of Fusion, J/g		79
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		420
Melting Completion (Liquidus), °C		1350

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		1300

Specific Heat Capacity, J/kg-K		230
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		60

Density, g/cm³		7.4
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		10

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		140

Embodied Water, L/kg		1210
Embodied Water, L/kg		230

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		19
Resilience: Unit (Modulus of Resilience), kJ/m³		54

Stiffness to Weight: Axial, points		4.2
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		22

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		7.5 to 8.5
Antimony (Sb), %		0

Arsenic (As), %		0 to 0.1
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.080
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 1.0

Copper (Cu), %		7.5 to 8.5
Copper (Cu), %		0 to 1.3

Iron (Fe), %		0 to 0.080
Iron (Fe), %		0 to 3.0

Lead (Pb), %		0 to 0.35
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.5

Nickel (Ni), %		0
Nickel (Ni), %		95 to 100

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 2.0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		82.3 to 85
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0