Grade 3 Babbitt Metal vs. C83800 Bronze

Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while C83800 bronze belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is C83800 bronze.

Grade 3 (L13840) Tin-Base Babbitt Metal UNS C83800 (Alloy 4B) Hydraulic Bronze

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		56
Elastic (Young's, Tensile) Modulus, GPa		100

Poisson's Ratio		0.35
Poisson's Ratio		0.34

Shear Modulus, GPa		21
Shear Modulus, GPa		39

Tensile Strength: Yield (Proof), MPa		46
Tensile Strength: Yield (Proof), MPa		110

Thermal Properties

Latent Heat of Fusion, J/g		79
Latent Heat of Fusion, J/g		180

Melting Completion (Liquidus), °C		420
Melting Completion (Liquidus), °C		1000

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		840

Specific Heat Capacity, J/kg-K		230
Specific Heat Capacity, J/kg-K		370

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		19

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		30

Density, g/cm³		7.4
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		2.9

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		47

Embodied Water, L/kg		1210
Embodied Water, L/kg		340

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		19
Resilience: Unit (Modulus of Resilience), kJ/m³		53

Stiffness to Weight: Axial, points		4.2
Stiffness to Weight: Axial, points		6.6

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		18

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0 to 0.0050

Antimony (Sb), %		7.5 to 8.5
Antimony (Sb), %		0 to 0.25

Arsenic (As), %		0 to 0.1
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.080
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		7.5 to 8.5
Copper (Cu), %		82 to 83.8

Iron (Fe), %		0 to 0.080
Iron (Fe), %		0 to 0.3

Lead (Pb), %		0 to 0.35
Lead (Pb), %		5.0 to 7.0

Nickel (Ni), %		0
Nickel (Ni), %		0 to 1.0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 1.5

Silicon (Si), %		0
Silicon (Si), %		0 to 0.0050

Sulfur (S), %		0
Sulfur (S), %		0 to 0.080

Tin (Sn), %		82.3 to 85
Tin (Sn), %		3.3 to 4.2

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		5.0 to 8.0

Residuals, %		0
Residuals, %		0 to 0.7