Grade 300 Maraging Steel vs. 92-silver 8-tin-oxide
Grade 300 maraging steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 6.5 to 18 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 62 to 110 |
| Shear Strength, MPa | 640 to 1190 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 120 to 300 |