Grade 300 Maraging Steel vs. ASTM A27 Cast Steel
Both grade 300 maraging steel and ASTM A27 cast steel are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is ASTM A27 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 6.5 to 18 | |
| 25 to 27 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 460 to 550 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 1.8 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 68 | |
| 18 |
| Embodied Water, L/kg | 150 | |
| 45 to 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 96 to 120 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 68 | |
| 16 to 20 |
| Strength to Weight: Bending, points | 28 to 43 | |
| 17 to 19 |
| Thermal Shock Resistance, points | 31 to 62 | |
| 15 to 18 |