Grade 300 Maraging Steel vs. Austenitic Nodular Cast Iron
Both grade 300 maraging steel and austenitic nodular cast iron are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is austenitic nodular cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 to 190 |
| Elongation at Break, % | 6.5 to 18 | |
| 6.8 to 34 |
| Poisson's Ratio | 0.3 | |
| 0.29 to 0.3 |
| Shear Modulus, GPa | 75 | |
| 70 to 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 430 to 500 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 190 to 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 to 350 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1340 to 1400 |
| Melting Onset (Solidus), °C | 1430 | |
| 1300 to 1360 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 to 490 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 to 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 16 to 25 |
| Density, g/cm3 | 8.2 | |
| 7.7 to 8.0 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 3.5 to 4.9 |
| Embodied Energy, MJ/kg | 68 | |
| 48 to 68 |
| Embodied Water, L/kg | 150 | |
| 91 to 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 24 to 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 35 to 68 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 28 to 43 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 31 to 62 | |
| 12 to 15 |