Grade 300 Maraging Steel vs. Nickel Beryllium 360
Grade 300 maraging steel belongs to the iron alloys classification, while nickel beryllium 360 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is nickel beryllium 360.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 6.5 to 18 | |
| 1.0 to 30 |
| Poisson's Ratio | 0.3 | |
| 0.3 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Shear Strength, MPa | 640 to 1190 | |
| 510 to 1100 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 780 to 1860 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 380 to 1590 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1480 | |
| 1330 |
| Melting Onset (Solidus), °C | 1430 | |
| 1200 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.3 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 12 to 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 68 | |
| 26 to 62 |
| Strength to Weight: Bending, points | 28 to 43 | |
| 23 to 41 |
| Thermal Shock Resistance, points | 31 to 62 | |
| 19 to 46 |